| BITUMEN 60/70 | |||
|---|---|---|---|
| Characteristic | Unit | value | Test Method |
| Specific Gravity @ 25/25 | ºC | ºC 1.01-1.06 | ASTM D-70 |
| Penetration @ 25 ºC | ºC | 60-70 | ASTM D-5 |
| Softening Point | ºC | 49-56 | ASTM D-36 |
| Ductility @ 25 ºC | ºC | 100 min | ASTM D-113 |
| Loss On Heating | %wt | 0.2 max | ASTM D-6 |
| Drop In Penetration After Heating % | --- | 20 max | ASTM D-6 & D-5 |
| Flash Point | ºC | 250 min | ASTM D-92 |
| Solubility In CS2 | %wt | 99.5 min | ASTM D-4 |
| Spot Test | ºC | negative | * A.A.S.H.O.T.102 |
| BITUMEN 80/100 | |||
|---|---|---|---|
| Characteristic | Unit | value | Test Method |
| Specific Gravity @ 25/25 | ºC | 1.00-1.05 | ASTM D-70 |
| Penetration @ 25 ºC | ºC | 80-100 | ASTM D-5 |
| Softening Point | ºC | 43 min | ASTM D-36 |
| Ductility @ 25 ºC | ºC | 100 min | ASTM D-113 |
| Flash Point | ºC | 225 min | ASTM D-92 |
| Solubility in Trichloroethylene | %wt | 99 min | ASTM D-4 |
| Loss on Heating | %wt | 0.5 max | ASTM D-6 |
| Drop In Penetration After Heating % | %%wt | Data20 max | ASTM D-6 & D-5 |
| Penetration Index | -- | -0.8 to +0.7 | -- |
| Spot Test | ºC | negative | * A.A.S.H.O.T.102 |